INOX 303 – A1 / 304 – A2 / 304L
Aciers inoxydables au Chrome / Nickel
| Appellation courante | Inox 303 | Inox A1 | Inox 304 | Inox 304 | Inox 304 | Inox A2 | Inox 304L | Inox 304L | Inox 304L |
| Désignation EN 10088-1 | 1.4305 | 1.4301 | 1.4307 | ||||||
| Désignation ASTM A240 | 304 | 304L | |||||||
| Désignation ASTM A351 | CF8 | CF3 | |||||||
| Désignation ISO 3506 (visserie) | A1 | A2 | |||||||
| Composition chimique (% en masse) | |||||||||
| C maxi | 0.1 | 0.12 | 0.07 | 0.08 | 0.08 | 0.1 | 0.03 | 0.03 | 0.03 |
| Cr mini - maxi | 17-19 | 16-19 | 17.5-19.5 | 18-20 | 18-21 | 15-20 | 17.5-19.5 | 18.-20 | 17-21 |
| Ni mini - maxi | 8-10 | 5-10 | 8-10.5 | 8-10.5 | 8-11 | 8-19 | 8-10.5 | 8-12 | 8.12 |
| Mo mini-maxi | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
| Si maxi | 1 | 1 | 1 | 0.75 | 2 | 1 | 1 | 0.75 | 2 |
| Mn maxi | 2 | 6.5 | 2 | 2 | 1.5 | 2 | 2 | 2 | 1.5 |
| P maxi | 0.045 | 0.2 | 0.045 | 0.045 | 0.04 | 0.05 | 0.045 | 0.045 | 0.04 |
| S maxi | 0.35 | 0.15-0.35 | 0.015 | 0.03 | 0.04 | 0.03 | 0.015 | 0.03 | 0.04 |
| N maxi | 0.11 | 0 | 0.11 | 0.1 | 0.2 | 0.2 | 0.11 | 0.1 | 0.2 |
| Cu maxi | 0-1 | 1.75-2.25 | 0 | 0 | 0 | 4 | 0 | 0 | 0 |
| Ti maxi | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
| Type d’inox | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique |
INOX 316 – A4 / 316L
Aciers inoxydables au Chrome / Nickel / Molybdène
| Appellation courante | 316 | 316 | 316 | 316 | A4 | 316L | 316L | 316L | 316L |
| Désignation EN 10088-1 | 1.4401 | 1.4408 | 1.4404 | 1.4435 | |||||
| Désignation ASTM A240 | 316 | 316L | |||||||
| Désignation ASTM A351 | CF8M | CF3M | |||||||
| Désignation ISO 3506 (visserie) | A4 | ||||||||
| Composition chimique (% en masse) | |||||||||
| C maxi | 0.07 | 0.08 | 0.07 | 0.08 | 0.08 | 0.03 | 0.03 | 0.03 | 0.03 |
| Cr mini - maxi | 16.5-18.5 | 16-18 | 18-20 | 18-21 | 16-18.5 | 16.5-18.5 | 16-18 | 17-19 | 17-21 |
| Ni mini - maxi | 10.-13 | 10-14 | 9-12 | 9-12 | 10-15 | 10-13 | 10-14 | 12.5-15 | 9-13 |
| Mo mini-maxi | 2-2.5 | 2-3 | 2-2.5 | 2-3 | 2-3 | 2-2.5 | 2-3 | 2.5-3 | 2.-3 |
| Si maxi | 1 | 0.75 | 1.5 | 1.5 | 1 | 1 | 0.75 | 1 | 1.5 |
| Mn maxi | 2 | 2 | 1.5 | 1.5 | 2 | 2 | 2 | 2 | 1.5 |
| P maxi | 0.045 | 0.045 | 0.04 | 0.04 | 0.045 | 0.045 | 0.045 | 0.045 | 0.04 |
| S maxi | 0.015 | 0.03 | 0.03 | 0.04 | 0.03 | 0.015 | 0.03 | 0.015 | 0.04 |
| N maxi | 0.11 | 0.1 | 0.2 | 0.2 | 0.2 | 0.11 | 0.1 | 0.11 | 0.2 |
| Cu maxi | 0 | 0 | 0.5 | 0 | 4 | 0 | 0 | 0 | 0 |
| Ti maxi | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
| Type d’inox | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique | Austénitique |
INOX 321 / 316 Ti
Aciers inoxydables au Chrome / Nickel / Titane
URANUS B6 / DUPLEX / INOX 309
Aciers inoxydables spéciaux
| Appellation courante | 321 | 321 | 316 Ti | 316 Ti | URANUS B6 | URANUS B6 | DUPLEX | 309 | 309 |
| Désignation EN 10088-1 | 1.4541 | 1.4571 | 1.4539 | 1.4462 | 1.4833 | ||||
| Désignation ASTM A240 | 321 | 316 Ti | 904L | 309S | |||||
| Composition chimique (% en masse) | |||||||||
| C maxi | 0.08 | 0.08 | 0.08 | 0.08 | 0.02 | 0.02 | 0.03 | 0.15 | 0.08 |
| Cr mini - maxi | 17-20 | 17-20 | 16.5-18.5 | 16-18 | 19-21 | 19-23 | 21-23 | 22-24 | 22-24 |
| Ni mini - maxi | 9-13 | 9-12 | 10.5-13.5 | 10-14 | 24-26 | 23-28 | 4.5-6.5 | 12-14 | 12-15 |
| Mo mini-maxi | 0 | 0 | 2-2.5 | 2-3 | 4-5 | 4-5 | 2.5-3.5 | 0 | 0 |
| Si maxi | 1 | 0.75 | 1 | 0.75 | 0.7 | 1 | 1 | 1 | 0.75 |
| Mn maxi | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 |
| P maxi | 0.040 | 0.045 | 0.045 | 0.045 | 0.03 | 0.045 | 0.035 | 0.045 | 0.045 |
| S maxi | 0.03 | 0.03 | 0.015 | 0.03 | 0.01 | 0.035 | 0.015 | 0.015 | 0.03 |
| N maxi | 0 | 0.1 | 0 | 0.1 | 0.15 | 0.1 | 0.1-0.22 | 0.11 | 0 |
| Cu maxi | 0 | 0 | 0 | 0 | 1.2-2 | 1-2 | 0 | 0 | 0 |
| Ti maxi | 5xC-0.7 | 5x(C+N)-0.7 | 5xC-0.7 | 5x(C+N)-0.7 | 0 | 0 | 0 | 0 | 0 |
| Type d’inox | Austénitique | Austénitique | Austénitique | Austénitique | Super Austénitique | Super Austénitique | Austéno-ferrique | Réfractaire | Réfractaire |
Ces tableaux donnent une liste non exhaustive des aciers inoxydables utilisés pour les produits présentés dans notre catalogue.
La composition chimique des différents inox est donnée à titre indicatif. Seule l’analyse matière et la norme de référence données sur les certificats font foi.
L’appellation courante est celle souvent utilisée dans les métiers liés à la robinetterie inox. Elle peut regrouper plusieurs inox ayant des caractéristiques similaires mais faits selon des normes différentes. Par exemple, l’appellation “inox 316L” regroupe la nuance 316L définie par le norme ASTM A240 et la nuance 1.4404 définie par la norme EN 10088-1.
Ces deux nuances peuvent être rigoureusement identiques ou bien légèrement différentes, car pour la composition chimique, les mini / maxi indiqués par les deux normes ne sont pas tout à fait les mêmes.
Avec l’évolution des normes et des directives européennes (DESP…), il est souvent nécessaire d’être plus précis en utilisant la désignation normalisée et sa norme de référence plutôt que l’appellation courante.